Brackets, structural parts, connectors and aerospace, medical and high-performance parts in titanium grade 5 (Ti-6Al-4V), milled and turned from your file. Upload your CAD and order online, starting at a single part.
Lightweight bracket
Titanium Grade 5 (Ti-6Al-4V) · 100 × 60 × 12 mm · 2 lightening pockets 30 × 40 × 8 · 4 Ø6.6 holes · CNC milled
1 pc
$199.60 USD
per part
25 pcs
$97.28 USD
per part
-51.26%100 pcs
$91.06 USD
per part
-54.38%Titanium grade 5 (Ti-6Al-4V, UNS R56400) is titanium alloyed with 6% aluminum and 4% vanadium. It takes 895 MPa in tension at a density of only 4.43 g/cm³, resists fatigue and corrosion, and can be heat treated. That is why it is used for brackets, structural parts, connectors and aerospace, medical and high-performance parts. At PREMSA we CNC mill and turn it from your file, starting at a single part with an instant price.
Titanium grade 5 (Ti-6Al-4V) properties: mechanical, physical and thermal data to choose the material for your machined part.
Material Type
Titanium Alloy (Ti-6Al-4V)
Primary Characteristics
High strength at low weight (895 MPa at 4.43 g/cm³), excellent fatigue and corrosion resistance, heat treatable, non-magnetic
Tensile Strength (Ultimate)
130 ksi (895 MPa)
Tensile Strength (Yield)
120 ksi (828 MPa)
Elongation at Break
10–14%
Hardness
≈ 330–360 HV (varies by condition)
Density
4.43 g/cm³ (0.160 lb/in³)
Elastic Modulus
16,500 ksi (114 GPa)
Poisson’s Ratio
0.34
Thermal Conductivity
6.7 W/m·K
Coefficient of Thermal Expansion
8.6 µm/m·°C
Melting Range
1600–1660 °C (2910–3020 °F)
Machinability
Difficult (18%): it conducts little heat and work hardens, so it is machined at low speed with sharp carbide tooling, a steady feed and plenty of coolant
Weldability
Good with inert gas shielding (TIG)
Formability
Limited when cold; it is hot formed
Corrosion Resistance
Excellent: resists seawater, chemicals and oxidation
Heat Treatment
Can be solution treated and aged to raise strength, or annealed for stress relief
Common Forms
Round bar, plate, billet and forgings
Typical Applications
Brackets, structural parts, connectors and fasteners, aerospace parts, medical parts, engine and high-performance parts
Material Composition
Titanium (Ti): Balance, Aluminum (Al): 5.5–6.75%, Vanadium (V): 3.5–4.5%, Iron (Fe): ≤0.40%, Oxygen (O): ≤0.20%
ASTM Standard
ASTM B348 / B265 / F136 (medical)
Rating across key engineering and manufacturing criteria.
Strength
Weight
Machinability
Weldability
Formability
Corrosion Resistance
Thermal Resistance
Cost Efficiency
Upload your CAD file and get an instant price and delivery date. CNC milling and turning from one part to production.
We CNC mill and turn titanium grade 5 parts that have to take load, fatigue and corrosion at low weight.
Lightweight brackets
Structural parts
Connectors and fasteners
Aerospace parts
Medical parts
Engine and racing parts
Flanges and fittings
Drone and robotics parts
Custom titanium grade 5 parts
What people ask most about titanium grade 5 parts: what it is, Ti-6Al-4V, composition, uses, machining, strength, weight, heat treatment, magnetism, corrosion, welding, equivalents, price and tolerances.
Titanium grade 5 is chosen for parts that have to take load and fatigue at low weight and in corrosive environments: brackets, structural parts, connectors and aerospace and medical parts.
At PREMSA Industries we machine titanium grade 5 with CNC milling and turning from your file, from a prototype to production.
Titanium grade 5 is chosen when the part has to take load and fatigue and stay light.
If your drawing doesn’t specify tolerances, we machine to ISO 2768-m (medium). On dimensions you call out —holes, pockets, fits and flatness— we can hold ±0.025 mm (±0.001 in), and critical dimensions are checked in inspection.
Titanium grade 5 is machined with CNC milling, CNC turning, drilling and tapping. It conducts little heat and work hardens, so it is cut at low speed, with a steady feed, sharp carbide tooling and plenty of coolant; lightening pockets are roughed in layers and finished with a light pass so thin walls and floors don’t distort.
Because it carries heavy loads at low weight, titanium grade 5 is used in many parts made with CNC machining.
Titanium grade 5 is usually the right choice when the part has to take load or fatigue, stay light and resist corrosion.